Specification

Fabric Specification
Fibre SpecificsPyrofil TR50S 12k
ColourBlack
Fibre Orientation0, 90
TypeComponent Prepreg
Resin MatrixEpoxy
Weave2 x 2 Twill
FormatWoven Fabric
Filament Count12k
Fibre TypeCarbon Fibre
BrandXPREG
Ends2.81cm
Picks2.81cm
Weight and Dimensions
Width1250mm
Consolidated Thickness0.45mm
Areal Weight450g/m²
Resin Weight38%
Fibre Properties
Max Cure Temp120°C
Max Service Temp130°C
UV ResistanceGood
Filament Diameter7µm
Min Cure Temp80°C
Out-life (at 20°C)30Days
Freezer-life (at -18°C)12Months
Typical Laminate Properties
Tensile Strength645MPa
Tensile Modulus55.2GPa
Compressive Strength615MPa
Flexural Strength882MPa
Flexural Modulus60.1GPa
Interlaminar Shear Strength69.8MPa
Tg Onset (DMA)140°C
Tg Peak (DMA)148°C
General Properties
Gross Weight1.22kg
BrandXPREG

Shipping Information

Restrictions

This product is not classed as dangerous goods for transport and can be shipped to all destinations without restriction.

Prepreg Product - IMPORTANT!

Uncured prepreg materials are stored at -20°C and are shipped still frozen from our facility. This prepreg has an 'out-life' of at least 30 days at room temperature and so typical delivery times will still leave plenty of safe 'out-life' remaining.

During summer months or periods of hot weather, it is recommended to order prepregs at the start of the week (Monday or Tuesday) to avoid adding extra shipping days over the weekend.

Unless you plan to use the product immediately, it should be placed into frozen storage as soon as possible on receipt.

Package Size

The packaged size of this product exceeds 1.2m in length and so an additional handling surcharge (charged by the courier) will be included in the quoted shipping cost.

Delivery Cost

To find the delivery cost of this item to your address, add it to your basket and then use the instant shipping calculator on the basket page.

XC130 450g 2x2 Twill 12k Prepreg Carbon Fibre (1250mm)

The backing ply for our XPREG® XC130 autoclave-cure prepreg carbon fibre system. This is an uncured prepreg material and requires an oven or autoclave to cure it.

This 450gsm 12k reinforcement uses a high strength TR50S fibre for maximum performance and 2x2 twill weave for excellent drape characteristics. It can be used on its own, in one or more plies, or together with lighter surface ply for the best possible surface finish.

This prepreg reinforcement is 1.25m (1250mm) wide and sold in a choice of prepacked roll lengths.


PRODUCT VERSIONS

Roll Length

AVAILABILITY:2 in stock available for immediate shipping

32 more can built in 2-3 days


PRICE
€93.80ex. VAT
(€75.04 /SQM)
2 in stock available for immediate shipping
QTY
ROLLS
ROLLS
We won’t be beaten on price!

If you believe you’re buying an equivalent product cheaper elsewhere, contact us to discuss your requirements.

XPREG® XC130 is an epoxy-based component prepreg system with a 130°C maximum service temperature developed for autoclave or other positive pressure cure.

This toughened resin system offers excellent mechanical properties whilst its clear formulation and excellent surface finish make it suitable for the manufacture of visual quality carbon fibre components. XC130 has a long out-life with an intermediate tack level making for easy handling and laminating whilst its variable cure temperature from 80°C allows a wide range of mould systems to be used.

XC130 is fully compatible with our XA120 adhesive film for the construction of complex composite structures, including honeycomb or foam cored laminates.

The autoclave prepreg carbon fibre backing 450g 12k material listed on this page is recommended for use as a backing ply, typically backing up a single layer of XC130 210g 3k Surface Ply.However autoclave prepreg carbon fibre 12k can be used in multiple layers where necessary although it can be beneficial to debulk the material for thicker laminates.

Typical Uses

XC130 is the recommended system for the manufacture of both structural and cosmetic applications where components will be cured in an autoclave or otherwise under positive pressure (such as heated platen press).

The combination of excellent mechanical performance, visual quality appearance and class-A surface finish make XC130 prepregs suitable for a wide range of applications from large-scale structural components to high-precision decorative parts.

High Performance

  • UAV/drones
  • Motorsport
  • Bike frames
  • Racing boats
  • Skis, boards

Large Scale

  • Boat hulls
  • Wind energy
  • Mass transit
  • Light aircraft

Cosmetic/Lifestyle

  • Interior trim
  • Phone cases
  • Furniture
  • Stands/display

How to Buy

All XPREG® prepregs are stored on site in our freezers. To reduce handling time and allow same-day dispatch, prepregs are available in pre-cut roll lengths. Choose the roll length you require from the drop-down list at the top of the page. When ordering a full roll of fabric the drop-down list shows the typical roll length but please allow for length variance of plus or minus 1m which has already been factored into the low unit price of our full length rolls.

Your XPREG® prepreg is sealed in air-tight packaging and will ship from us still frozen. Please see the transport tab for further details and important information about delivery.

The Sample Pack Contains two 400x300mm (15.7x11.8") pieces of pre-preg.

Further Information

Curing

XPREG® XC130 is designed to be autoclave cured or otherwise cured under positive pressure (such as heated platen or pressurised bladder).

Initial cure is possible from 80°C although service temperature will be determined by the final cure temperature.

CURE CYCLES AND RESULTING Tg

Cure Temp Comments Initial Min Cure Time Resulting Tg
80°C (Minimum) 16hrs 90°C
90°C 8hrs 100°C
100°C 4hrs 110°C
120°C (Maximum) 2hrs 120°C
130°C Post Cure 2hrs 140°C

Suitable Moulds/Tooling

Moulds/tools should be epoxy-based composite moulds, epoxy tooling board or metal. In all cases, moulds must be temperature stable to a minimum of 85°C but ideally to 120°C.

Fully Compatible:

  • High temp epoxy hand-layup moulds (e.g. EG160 / EMP160)
  • Carbon or glass fibre prepreg moulds (e.g. XPREG® XT135)
  • Epoxy tooling board (e.g. EB700 Epoxy Tooling Board with S120 Board Sealer)
  • Aluminium / stainless steel moulds
  • Toughened glass (for flat sheet/panels)

It is not recommended to use hand laminated Uni-Mould tools in an autoclave due to the likelihood that voids within the moulds will cause blisters and distortion in the mould at elevated temperature and pressure.

Storage and Handling

When not in use, XPREG® prepregs should be kept frozen at -18°C (0°F) in sealed plastic packaging. When ready to use, the material should be removed from the freezer and allowed to thaw fully to room temperature before being removed from the packaging.

Remaining material should be re-sealed before returning to the freezer to avoid the risk of moisture uptake.

XPREG® XC130 is an epoxy-based component prepreg system with a 130°C maximum service temperature developed for autoclave or other positive pressure cure.

This toughened resin system offers excellent mechanical properties whilst its clear formulation and excellent surface finish make it suitable for the manufacture of visual quality carbon fibre components. XC130 has a long out-life with an intermediate tack level making for easy handling and laminating whilst its variable cure temperature from 80°C allows a wide range of mould systems to be used.

XC130 is fully compatible with our XA120 adhesive film for the construction of complex composite structures, including honeycomb or foam cored laminates.

The autoclave prepreg carbon fibre backing 450g 12k material listed on this page is recommended for use as a backing ply, typically backing up a single layer of XC130 210g 3k Surface Ply.However autoclave prepreg carbon fibre 12k can be used in multiple layers where necessary although it can be beneficial to debulk the material for thicker laminates.

Typical Uses

XC130 is the recommended system for the manufacture of both structural and cosmetic applications where components will be cured in an autoclave or otherwise under positive pressure (such as heated platen press).

The combination of excellent mechanical performance, visual quality appearance and class-A surface finish make XC130 prepregs suitable for a wide range of applications from large-scale structural components to high-precision decorative parts.

High Performance

  • UAV/drones
  • Motorsport
  • Bike frames
  • Racing boats
  • Skis, boards

Large Scale

  • Boat hulls
  • Wind energy
  • Mass transit
  • Light aircraft

Cosmetic/Lifestyle

  • Interior trim
  • Phone cases
  • Furniture
  • Stands/display

How to Buy

All XPREG® prepregs are stored on site in our freezers. To reduce handling time and allow same-day dispatch, prepregs are available in pre-cut roll lengths. Choose the roll length you require from the drop-down list at the top of the page. When ordering a full roll of fabric the drop-down list shows the typical roll length but please allow for length variance of plus or minus 1m which has already been factored into the low unit price of our full length rolls.

Your XPREG® prepreg is sealed in air-tight packaging and will ship from us still frozen. Please see the transport tab for further details and important information about delivery.

The Sample Pack Contains two 400x300mm (15.7x11.8") pieces of pre-preg.

Further Information

Curing

XPREG® XC130 is designed to be autoclave cured or otherwise cured under positive pressure (such as heated platen or pressurised bladder).

Initial cure is possible from 80°C although service temperature will be determined by the final cure temperature.

CURE CYCLES AND RESULTING Tg

Cure Temp Comments Initial Min Cure Time Resulting Tg
80°C (Minimum) 16hrs 90°C
90°C 8hrs 100°C
100°C 4hrs 110°C
120°C (Maximum) 2hrs 120°C
130°C Post Cure 2hrs 140°C

Suitable Moulds/Tooling

Moulds/tools should be epoxy-based composite moulds, epoxy tooling board or metal. In all cases, moulds must be temperature stable to a minimum of 85°C but ideally to 120°C.

Fully Compatible:

  • High temp epoxy hand-layup moulds (e.g. EG160 / EMP160)
  • Carbon or glass fibre prepreg moulds (e.g. XPREG® XT135)
  • Epoxy tooling board (e.g. EB700 Epoxy Tooling Board with S120 Board Sealer)
  • Aluminium / stainless steel moulds
  • Toughened glass (for flat sheet/panels)

It is not recommended to use hand laminated Uni-Mould tools in an autoclave due to the likelihood that voids within the moulds will cause blisters and distortion in the mould at elevated temperature and pressure.

Storage and Handling

When not in use, XPREG® prepregs should be kept frozen at -18°C (0°F) in sealed plastic packaging. When ready to use, the material should be removed from the freezer and allowed to thaw fully to room temperature before being removed from the packaging.

Remaining material should be re-sealed before returning to the freezer to avoid the risk of moisture uptake.

Downloads (4)

Safety Datasheet (SDS)296 KB
Technical Datasheet (TDS)550 KB
Pyrofil TR Series Datasheet354 KB
XPREG Price List789 KB

Specification

Fabric Specification
Fibre SpecificsPyrofil TR50S 12k
ColourBlack
Fibre Orientation0, 90
TypeComponent Prepreg
Resin MatrixEpoxy
Weave2 x 2 Twill
FormatWoven Fabric
Filament Count12k
Fibre TypeCarbon Fibre
BrandXPREG
Ends2.81cm
Picks2.81cm
Weight and Dimensions
Width1250mm
Consolidated Thickness0.45mm
Areal Weight450g/m²
Resin Weight38%
Fibre Properties
Max Cure Temp120°C
Max Service Temp130°C
UV ResistanceGood
Filament Diameter7µm
Min Cure Temp80°C
Out-life (at 20°C)30Days
Freezer-life (at -18°C)12Months
Typical Laminate Properties
Tensile Strength645MPa
Tensile Modulus55.2GPa
Compressive Strength615MPa
Flexural Strength882MPa
Flexural Modulus60.1GPa
Interlaminar Shear Strength69.8MPa
Tg Onset (DMA)140°C
Tg Peak (DMA)148°C
General Properties
Gross Weight1.22kg
BrandXPREG
Can’t find the answer you’re looking for?Ask our technical team a question.

Unfortunately we do not stock any pre-pregs with a flexible resin. The only flexible resin we supply is our EF80 Flexible Epoxy Resin which is suitable for wet lay and vacuum bagged processes.

To achieve a good quality pinhole free cosmetic finish, we would recommend at least 3 bar as the minimum pressure applied during the curing process.

ASK YOUR OWN QUESTION

Note: Your name will be abbreviated and your email address will only be used to email you the answer directly

Note: Your name will be abbreviated and your email address will only be used to email you the answer directly

Customer Product Reviews for XC130 450g 2x2 Twill 12k Prepreg Carbon Fibre (1250mm)

No reviews

SUBMIT YOUR OWN PRODUCT REVIEW

We publish all reviews for verified purchases. Submit your own review and help other customers with their choices.

SUBMIT YOUR OWN PRODUCT REVIEW

We publish all reviews for verified purchases. Submit your own review and help other customers with their choices.

Shipping Information

Restrictions

This product is not classed as dangerous goods for transport and can be shipped to all destinations without restriction.

Prepreg Product - IMPORTANT!

Uncured prepreg materials are stored at -20°C and are shipped still frozen from our facility. This prepreg has an 'out-life' of at least 30 days at room temperature and so typical delivery times will still leave plenty of safe 'out-life' remaining.

During summer months or periods of hot weather, it is recommended to order prepregs at the start of the week (Monday or Tuesday) to avoid adding extra shipping days over the weekend.

Unless you plan to use the product immediately, it should be placed into frozen storage as soon as possible on receipt.

Package Size

The packaged size of this product exceeds 1.2m in length and so an additional handling surcharge (charged by the courier) will be included in the quoted shipping cost.

Delivery Cost

To find the delivery cost of this item to your address, add it to your basket and then use the instant shipping calculator on the basket page.

100% SECURE

    Secured by Digicert Payment processing by Adyen

PAYMENT METHODS

    Mastercard logo Visa logo Maestro logo Ideal logo Carte Bancaire logo Giropay logo Bancontact logo PayPal logo Bank transfer logo

Easy Composites EU B.V., registered in the Netherlands 73601195. All content copyright (C) Easy Composites Ltd, 2024. All rights reserved.