VM100 Black 10min Methyl Methacrylate Adhesive

Yes, certainly. In fact the easiest way to do this is to simply leave the static mixer nozzle in place after you use the adhesive. The adhesive that's in the nozzle will have been mixed and so will cure but the glue at the start of the nozzle will be unmixed and not cured meaning the nozzle will twist off perfectly and the glue inside will have been protected from the atmosphere and so will be perfectly preserved ready for use.

A typical application of the adhesive is approximately a 0.5mm thick layer. At this thickness, one 50ml cartridge would cover an area 30cm by 30cm; a 400ml cartridge would cover an area approximately 90cm by 90cm.

For best results when gluing over a large surface area, use a spreader to help ensure the adhesive is laid down in an even layer.

There is no practical minimum bond thickness for this adhesive although you do need to ensure that *some* adhesive is present, which is why glass spheres are sometimes used to prevent the adhesive from being scraped off completely. Essentially though, as long as an even thin film is applied the bond strength between the two materials will be good.

Nylon, in common with many inert thermoplastics, can be difficult to bond to, even with the modern generation of structural adhesives. However, it is possible to bond with VM100 if you “flame treat” the nylon just prior to adhesive application. The flame treatment helps the adhesive get the best bond possible to the nylon

If you're using the VM100 as the adhesive, your best best would probably be ABS as it can be bonded with the VM100 and should stand up to the temperatures that you might experience in your car.  

No, unfortunately VM100 Black is not designed to stick any rubber or silicone materials. Silicone is particular can be a very difficult material to bond to and will almost always require a specialist silicone adhesive.

Yes, our VM100B is highly UV resistant.

The VM100 makes an excellent adhesive for bonding tabs on test tokens. In our own laboratory we also use ET515 Semi Flexible 15min Professional Epoxy Adhesive for some tests where more flexural strength is required.

Plexus is an adhesive manufacturer who are best know for their methacrylate adhesives. VuduGlu VM100 is also a methacrylate adhesive (an MMA) which is similar to some Plexus MMAs although it is not manufactured by Plexus and does not directly match any of their product variants.

VM100 Black will bond reasonably well to ABS. It would be important to key the surface and give it a thorough clean before bonding.

Yes, VM100 Black is a very diverse adhesive and can bond a variety of materials. Aluminium to aluminium with VM100 will give a good strong bond. Both surfaces will need a good key and a thorough clean to achieve the best results.

VM100 is not electrically conductive in its natural form. Like many adhesives and resins, conductivity can be very fractionally improved through the addition of metallic particles and/or carbon fibres, however the resistance is extremely high in these circumstances.

Once fully cured you will have no problems sanding and shaping the cured adhesive as necessary.

Yes, VM100 Black would make a good adhesive for this application. The bond strength to aluminium and carbon fibre would both be excellent, subject to appropriate preparation (de-greasing, keying).

We would recommend our VM100 Black 10min Methacrylate Adhesive; it has excellent bond strength between aluminium and carbon fibre.

The cap on the VM100 is removed by initially snapping the cap off leaving the exposed nozzle.

Once you have finished with using the glue, the snapped off cap is turned upside down and will fit over the glue tube by pressing on and rotating 90 degrees clockwise to seal.